• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Dissertação de Mestrado
DOI
10.11606/D.18.2018.tde-14062018-144401
Documento
Autor
Nome completo
Janice Mesquita Teodoro
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1999
Orientador
Banca examinadora
Bueno, Benedito de Souza (Presidente)
Consoli, Nilo Cesar
Nogueira, João Baptista
Título em português
Resistência ao cisalhamento de solos reforçados com fibras plásticas
Palavras-chave em português
Compósitos de solos
Fibras de polipropileno
Fibras plásticas
Reforço de solo
Resumo em português
Este trabalho aborda o comportamento de dois solos (uma argila e uma areia), reforçados com fibras plásticas de polipropileno. Os solos foram compactados no teor de umidade ótimo e peso específico seco máximo e foram misturados com fibras de diferentes teores e comprimentos. Os resultados dos ensaios de compressão simples foram usados para selecionar os teores e comprimentos ótimos de fibras. Os resultados mostraram que a resistência do solo arenoso cresceu com o aumento do teor e comprimento das fibras e o solo argiloso apresentou acréscimo de resistência, com o aumento do teor até o comprimento de fibra de 10 mm. As curvas tensão-deformação dos ensaios triaxiais, para solos com e sem reforço foram similares, com uma resistência de pico definida e pequena redução de queda de tensão pós pico. As amostras de solo arenoso apresentaram considerável aumento de resistência, com o aumento do teor e comprimento das fibras. Pequenos painéis, fabricados com o solo argiloso (300 x 300 x 100) mm, mostraram que a presença da fibra pode reduzir a magnitude das trincas quando comparados com o solo sem reforço.
Título em inglês
not available
Palavras-chave em inglês
Plastic fibers
Polypropylene fibers
Soil reinforcement
Soils composites
Resumo em inglês
This work presents the behavior of two soils (clay and sandy) reinforced with polypropylene plastic fibers. The soils were compacted at the optimum moisture content and maximum dry unit weight and were mixed with fibers of different lengths and contents. Unconfined compressive tests results were used to select the optimum fiber length and content. The results showed that the granular soil strength increased with increasing fiber length and content. The cohesive soil, on the other hand, showed strength up to fiber length of 10 mm. Stress - strain curves from triaxial tests for both reinforced and unreinforced cohesive soil were similar with a defined peak strength and small post peak reduction. Granular soil samples presented considerable strength increases with the increases of length and fiber content. Small panels fabricated with the reinforced cohesive soil (300 x 300 x 100) mm, showed that the presence of fiber can reduce crack magnitude when compared with the unreinforced soil.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2018-06-14
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2018. Todos os direitos reservados.